Research on water-line corrosion of carbon steel by wire beam electrode technique
The wire beam electrode (WBE) method was employed to study water-line corrosion of carbon steel under static condition. It was found that, it was the thin electrolyte film that aggravated the corrosion of steel in water-line area, not the difference of oxygen concentration. The difference of oxygen...
Main Authors: | , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
EDP Sciences
2016-01-01
|
Series: | MATEC Web of Conferences |
Online Access: | http://dx.doi.org/10.1051/matecconf/20163901004 |
id |
doaj-658169de7b5a47cfa7a0a7486e46315a |
---|---|
record_format |
Article |
spelling |
doaj-658169de7b5a47cfa7a0a7486e46315a2021-03-02T08:59:51ZengEDP SciencesMATEC Web of Conferences2261-236X2016-01-01390100410.1051/matecconf/20163901004matecconf_iccme2016_01004Research on water-line corrosion of carbon steel by wire beam electrode techniqueChen YalinZhang WeiDing Jian0Yin PengfeiWang Jia1Zou Yan2College of Chemistry and Chemical Engineering, Ocean University of ChinaCollege of Chemistry and Chemical Engineering, Ocean University of ChinaInstitute of Oceanographic Instrumentation, Shandong Provincial Key Laboratory of Ocean Environment Monitoring TechnologyThe wire beam electrode (WBE) method was employed to study water-line corrosion of carbon steel under static condition. It was found that, it was the thin electrolyte film that aggravated the corrosion of steel in water-line area, not the difference of oxygen concentration. The difference of oxygen concentration decided the location of cathode, which was near waterline, and the regularity of vertical current distribution under waterline. Besides, it was also found that, in water-line area, the peak of corrosion rate was located at about half of the region just below the waterline.http://dx.doi.org/10.1051/matecconf/20163901004 |
collection |
DOAJ |
language |
English |
format |
Article |
sources |
DOAJ |
author |
Chen Yalin Zhang Wei Ding Jian Yin Pengfei Wang Jia Zou Yan |
spellingShingle |
Chen Yalin Zhang Wei Ding Jian Yin Pengfei Wang Jia Zou Yan Research on water-line corrosion of carbon steel by wire beam electrode technique MATEC Web of Conferences |
author_facet |
Chen Yalin Zhang Wei Ding Jian Yin Pengfei Wang Jia Zou Yan |
author_sort |
Chen Yalin |
title |
Research on water-line corrosion of carbon steel by wire beam electrode technique |
title_short |
Research on water-line corrosion of carbon steel by wire beam electrode technique |
title_full |
Research on water-line corrosion of carbon steel by wire beam electrode technique |
title_fullStr |
Research on water-line corrosion of carbon steel by wire beam electrode technique |
title_full_unstemmed |
Research on water-line corrosion of carbon steel by wire beam electrode technique |
title_sort |
research on water-line corrosion of carbon steel by wire beam electrode technique |
publisher |
EDP Sciences |
series |
MATEC Web of Conferences |
issn |
2261-236X |
publishDate |
2016-01-01 |
description |
The wire beam electrode (WBE) method was employed to study water-line corrosion of carbon steel under static condition. It was found that, it was the thin electrolyte film that aggravated the corrosion of steel in water-line area, not the difference of oxygen concentration. The difference of oxygen concentration decided the location of cathode, which was near waterline, and the regularity of vertical current distribution under waterline. Besides, it was also found that, in water-line area, the peak of corrosion rate was located at about half of the region just below the waterline. |
url |
http://dx.doi.org/10.1051/matecconf/20163901004 |
work_keys_str_mv |
AT chenyalin researchonwaterlinecorrosionofcarbonsteelbywirebeamelectrodetechnique AT zhangwei researchonwaterlinecorrosionofcarbonsteelbywirebeamelectrodetechnique AT dingjian researchonwaterlinecorrosionofcarbonsteelbywirebeamelectrodetechnique AT yinpengfei researchonwaterlinecorrosionofcarbonsteelbywirebeamelectrodetechnique AT wangjia researchonwaterlinecorrosionofcarbonsteelbywirebeamelectrodetechnique AT zouyan researchonwaterlinecorrosionofcarbonsteelbywirebeamelectrodetechnique |
_version_ |
1724240180224720896 |