Plastic behaviour and forming limit during biaxial compressions of magnesium alloy AZ31 at room temperature
The plastic behaviour and compressive fracture of AZ31 magnesium alloy were examined at room temperature. The uniaxial compression tests and biaxial compression tests along linear and nonlinear strain paths were carried out until fracture using a unique biaxial compression testing machine develop...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2010-06-01
|
| Series: | EPJ Web of Conferences |
| Online Access: | http://dx.doi.org/10.1051/epjconf/20100616001 |
| Summary: | The plastic behaviour and compressive fracture of AZ31 magnesium alloy were examined at room temperature. The uniaxial compression tests and biaxial compression tests along linear and nonlinear strain paths were carried out until fracture using a unique biaxial compression testing machine developed by author. The results revealed the evolution of plastic anisotropy in biaxial compressions, that is the strain path dependency of work hardening. The adaptability of several forming limit criteria to the compressive fracture of AZ31 alloy was discussed. It was found that the uniform estimation of compressive forming limits by uniaxial and biaxial compressions was difficult by Freudenthal criterion and Oyane criterion. The result of Tresca energy criterion suggested that the criterion based on shear stress has possibility to predict the compressive forming limits at room temperature of AZ31 alloy. |
|---|---|
| ISSN: | 2100-014X |