| Summary: | The commonly used curing system for chloroprene rubber (CR) is a combination of two metal oxides, such as magnesium oxide (MgO) and zinc oxide (ZnO). Application of MgO and ZnO enables to obtain a good balance between processability of rubber compounds and mechanical properties of the vulcanizates. Despite high activity in crosslinking reactions, ZnO is classified as ecotoxic to aquatic organisms, thus environmental legislation requires its quantity in technology to be limited. In our studies more environmentally friendly curing systems were applied, which enabled eliminating ZnO from CR compounds. These curing systems consisted of manganese acetylacetonate (Mn(acac)) or nickel acetylacetonate (Ni(acac)) and triethanolamine (TEOA) used as a base necessary to perform Heck’s reaction. Both metal acetylacetonates exhibited high activity in crosslinking reactions, which was confirmed by a great torque increment during rheometric measurements and high degree of elastomer crosslinking. The type of metal acetylacetonate and the amount of TEOA seemed to have less influence on the efficiency of the curing system than the filler used. Rubber compounds filled with carbon black (CB) were characterized by definitely shorter optimal vulcanization times and higher degree of crosslinking compared to CR composites filled with nanosized SiO<sub>2</sub>. Moreover, application of the proposed curing systems allowed to obtain CR vulcanizates with mechanical properties comparable with the benchmarks cured with metal oxides.
|
|---|