Tunable Band Gap Energy of Mn-Doped ZnO Nanoparticles Using the Coprecipitation Technique
A simple coprecipitation technique was introduced to form manganese (Mn) doped on zinc oxide (ZnO) nanoparticles effectively. Based on our morphological studies, it was revealed that mean particle size was increased while bigger agglomeration of nanoparticles could be observed as the amount of conce...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2014-01-01
|
| Series: | Journal of Nanomaterials |
| Online Access: | http://dx.doi.org/10.1155/2014/371720 |
| Summary: | A simple coprecipitation technique was introduced to form manganese (Mn) doped on zinc oxide (ZnO) nanoparticles effectively. Based on our morphological studies, it was revealed that mean particle size was increased while bigger agglomeration of nanoparticles could be observed as the amount of concentration of Mn was increased. Interestingly, it was found that the position of the absorption spectra was shifted towards the lower wavelength (UV region) as correlated with the increasing of Mn dopants concentration into ZnO nanoparticles. This result inferred that optimum content of Mn doped into the ZnO nanoparticles was crucial in controlling the visible/UV-responsive of samples. In the present study, 3 mol% of Mn dopants into the ZnO nanoparticles exhibited the better UV as well as visible light-responsive as compared to the other samples. The main reason might be attributed to the modification of electronic structure of ZnO nanoparticles via lattice doping of Mn ions into the lattice, whereas excessive Mn dopants doped on ZnO nanoparticles caused the strong UV-responsive due to the more 3d orbitals in the valence band. |
|---|---|
| ISSN: | 1687-4110 1687-4129 |