EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS

EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS

In this study, steel sheet materials were used in order to obtain dual-phase steel. Specimens for this purpose have been annealed in ferrite + astatine regions at the temperatures of 740, 760, 800 and 820 °C. The specimens were annealed at the different temperatures with corresponding times 20, 4...

Full description

Bibliographic Details
Main Author: Ali BAYRAM
Format: Article
Language:English
Published: Pamukkale University 1998-03-01
Series:Pamukkale University Journal of Engineering Sciences
Subjects:
Dual faz, Martenzit, Yükleme hızı
Online Access:http://dergipark.ulakbim.gov.tr/pajes/article/view/5000090016
id doaj-6cf5d7f60c33463b88ddfed505f597a0
record_format Article
spelling doaj-6cf5d7f60c33463b88ddfed505f597a02020-11-25T00:19:55ZengPamukkale UniversityPamukkale University Journal of Engineering Sciences1300-70092147-58811998-03-01436926975000084084EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELSAli BAYRAMIn this study, steel sheet materials were used in order to obtain dual-phase steel. Specimens for this purpose have been annealed in ferrite + astatine regions at the temperatures of 740, 760, 800 and 820 °C. The specimens were annealed at the different temperatures with corresponding times 20, 40 and 60 minutes and quenched into water. As a result of this dual-phase steels at different ferrite + martensite ratio were produced. Sheet specimens were tested at the range of loading rates of 10, 50 and 259 mm/min. Strength properties of dual-phase steels were investigated depending on annealing temperature, ratio of martensite and loading rate.http://dergipark.ulakbim.gov.tr/pajes/article/view/5000090016Dual faz, Martenzit, Yükleme hızı
collection DOAJ
language English
format Article
sources DOAJ
author Ali BAYRAM
spellingShingle Ali BAYRAM
EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS
Pamukkale University Journal of Engineering Sciences
Dual faz, Martenzit, Yükleme hızı
author_facet Ali BAYRAM
author_sort Ali BAYRAM
title EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS
title_short EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS
title_full EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS
title_fullStr EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS
title_full_unstemmed EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS
title_sort effect of mechanical properties of martensite and loading rate on dual phase steels
publisher Pamukkale University
series Pamukkale University Journal of Engineering Sciences
issn 1300-7009
2147-5881
publishDate 1998-03-01
description In this study, steel sheet materials were used in order to obtain dual-phase steel. Specimens for this purpose have been annealed in ferrite + astatine regions at the temperatures of 740, 760, 800 and 820 °C. The specimens were annealed at the different temperatures with corresponding times 20, 40 and 60 minutes and quenched into water. As a result of this dual-phase steels at different ferrite + martensite ratio were produced. Sheet specimens were tested at the range of loading rates of 10, 50 and 259 mm/min. Strength properties of dual-phase steels were investigated depending on annealing temperature, ratio of martensite and loading rate.
topic Dual faz, Martenzit, Yükleme hızı
url http://dergipark.ulakbim.gov.tr/pajes/article/view/5000090016
work_keys_str_mv AT alibayram effectofmechanicalpropertiesofmartensiteandloadingrateondualphasesteels
_version_ 1725369804017106944

Similar Items