DC-bias and visible light effect on dielectric characteristics of La0.5Cr0.5TiO3+δ
La0.5Cr0.5TiO3+δ ceramic sample was prepared via traditional solid-state reaction route. Frequency and temperature dependence of dielectric permittivity were studied in the range of 102 ~ 106 Hz and of 77 ~ 360 K, respectively. It was observed that extraordinarily high low-frequency dielectric co...