Assessment of the Impact of Hydraulic Binder on the Properties of the Cold Recycled Mixture with Foamed Bitumen and Bitumen Emulsion: Field Tests

• Main Authors: Przemysław Buczyński, Marek Iwański, Jakub Krasowski
• Format: Article
• Language: English
• Published: MDPI AG 2020-11-01
• Series: Buildings
• Subjects: foamed bitumen; bitumen emulsion; cold-recycled mixture; hydraulic binder; durability
• Online Access: https://www.mdpi.com/2075-5309/10/12/223

The paper presents the results of tests of the impact of hydraulic and bituminous binders on the properties of the cold-recycled mixture (CRM). The composition of the cold-recycled mixture includes two types of different binders, i.e., bituminous binder in the form of foamed bitumen and bitumen emulsion, as well as Portland cement (CEM I 32.5R) and hydraulic binder. The hydraulic binder was produced by mixing three base ingredients in the following ratio: 40% CEM I 32.5R; 20% Ca(OH)₂ and 40% CBD (cement bypass dust). The cold-recycled mixtures were produced under industrial conditions on a test section. The prepared CRM with bitumen emulsion (MCE) and foamed bitumen (MCAS) was collected from the test section and compacted under laboratory conditions. The impact of the type and kind of the binder was assessed in terms of physical properties, mechanical properties and deformation modulus (bearing capacity of subbase) of the recycled base course after 1, 7 and 28 days. It was found that the use of hydraulic binder in the recycled base course, regardless of the type of bituminous binder, reduced cohesion without reducing the remaining parameters.