The Effect Of Homogenization Conditions On The Structure And Properties Of 6082 Alloy Billets

• Main Authors: Woźnicki A., Leśniak D., Włoch G., Leszczyńska-Madej B., Wojtyna A.
• Format: Article
• Language: English
• Published: Polish Academy of Sciences 2015-09-01
• Series: Archives of Metallurgy and Materials
• Subjects: 6082 alloy; homogenization temperature; cooling rate after homogenization
• Online Access: http://www.degruyter.com/view/j/amm.2015.60.issue-3/amm-2015-0303/amm-2015-0303.xml?format=INT

The paper presents the results of laboratory homogenization investigations of the 6082 grade alloys, differing in Mg and Si content. At the first stage, the microstructure of alloys was analysed after homogenization finished with water quenching. SEM/EDS investigations and DSC tests were applied to evaluate the dissolution of the Mg2Si particles and concentration of the main alloying additions in the grains interiors, depending on soaking conditions. In the case of alloy with lower Mg and Si content, homogenization the temperature of 535ºC for 8h is sufficient for significant Mg2Si particles dissolution. For the alloy with higher Mg and Si content, after homogenization the temperature of 550ºC for 8h, the amount of undissolved Mg2Si particles decreases visibly, compared to homogenization at 535ºC for 8h. However, an unfavourable tendency of dispersoids growth is observed and these soaking conditions are not found to be recommended.