Dependency of microstructure and microhardness on withdrawal rate of Ti-43Al-2Cr-2Nb alloy prepared by electromagnetic cold crucible directional solidification
The intermetallic Ti-43Al-2Cr-2Nb (at.%) alloy was directionally solidified in an electromagnetic cold crucible with different withdrawal rates (V) ranging from 0.2 to 1.0 mm昺in-1, at a constant temperature gradients (G=18 K昺m-1) . Macrostructures of the alloy were observed by optical microscopy. Mi...
Main Authors: | Yong-zhe Wang, Hong-sheng Ding, Rui-run Chen |
---|---|
Format: | Article |
Language: | English |
Published: |
Foundry Journal Agency
2016-07-01
|
Series: | China Foundry |
Subjects: | |
Online Access: | http://ff.foundryworld.com/uploadfile/2016080937088885.pdf |
Similar Items
-
Progress in research on cold crucible directional solidification of titanium based alloys
by: Chen Ruirun, et al.
Published: (2014-07-01) -
Microstructure formation and columnar to equiaxed transition during cold crucible directional solidification of a high-Nb TiAl alloy
by: Xuesong Xu, et al.
Published: (2021-03-01) -
High-temperature deformation resistance and creep resistance of a TiAl-based alloy fabricated by cold crucible directional solidification technology
by: Shu-lin Dong, et al.
Published: (2020-09-01) -
Microstructure and microhardness of Ti-48Al alloy prepared by rapid solidification
by: Xiao-yu Chen, et al.
Published: (2020-11-01) -
Microstructures, micro-segregation and solidification path of directionally solidified Ti-45Al-5Nb alloy
by: Liang-shun Luo, et al.
Published: (2016-03-01)