Research on testing method of resin sand high temperature compressive strength

• Main Authors: Peng Wan, Luan-cai Li, Long Zhang
• Format: Article
• Language: English
• Published: Foundry Journal Agency 2016-09-01
• Series: China Foundry
• Subjects: resin sand; high temperature compressive strength; hollow cylinder specimens;variation coefficient
• Online Access: http://ff.foundryworld.com/uploadfile/2016101358898257.pdf

High temperature compressive strength is one of the most important performances of resin sand; its value directly concerns the quality of castings. In order to seek the best testing method of resin sand high temperature compressive strength, a self-developed instrument was used to carry out experiments, and the sample shape and size were designed and studied. The results show that a hollow cylinder sample can reflect the strength difference of different resin sands better than a solid cylinder sample, and its data is stable. The experiments selected フ20/5】30 mm as the size of the hollow cylinder samples. The high temperature compressive strengths of phenol-formaldehyde resin coated sand, furan resin self-setting sand, and TEA resin sand were each tested. For the resin sand used for cast steel and cast iron, 1,000 ìC was selected as the test temperature; for the resin sand used for cast non-ferrous alloy, 800 ìC was selected as the test temperature; and for all the resin sand samples, 1 min was selected as the holding time. This testing method can truthfully reflect the high temperature performance of three kinds of resin sand; it is reproducible, and the variation coefficients of test values are under 10%.