Effects of an Alternating Magnetic Field/Ag Multi-Alloying Combined Solidification Process on Cu–14Fe Alloy
An alternating magnetic field (AMF)/Ag multi-alloying combined process was applied to the solidification of Cu⁻14Fe alloy to study its effects on the microstructure and properties of the resulting samples. The applied AMF and Ag multi-alloying had positive effects on the refinement of the...
Main Authors: | Jin Zou, De-Ping Lu, Ke-Ming Liu, Qing-Feng Fu |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2018-12-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/11/12/2501 |
Similar Items
-
Influences of Alternating Magnetic Fieldson the Growth Behavior and Distribution of the Primary Fe Phasein Cu-14Fe Alloys during the Solidification Process
by: Jin Zou, et al.
Published: (2018-07-01) -
Development of New High Strength Alloy in Cu-Fe-Si System through Rapid Solidification
by: Sarkar, Suman
Published: (2018) -
Co-Precipitation, Strength and Electrical Resistivity of Cu–26 wt % Ag–0.1 wt % Fe Alloy
by: Rui Li, et al.
Published: (2017-12-01) -
Effects of Mg Content on the Microstructural and Mechanical Properties of Al-4Cu-<i>x</i>Mg-0.3Ag Alloys
by: Talal T. Alshammari, et al.
Published: (2020-10-01) -
STRUCTURE REFINEMENT PECULARITIES AND SOLID SOLUTION FORMATION IN THE CAST Cu-Fe ALLOY, SUBJECTED TO SEVERE PLASTIC DEFORMATION
by: A.V. Lukyanov, et al.
Published: (2014-11-01)