Liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass
Glass-ceramics were produced utilizing fly-ash from coal power stations and waste glass of TV monitors, windows and flask glass. The powder technology route was employed. The mixture of 50% fly ash and 50% waste TV glass increases the bending strength from 12±1 to 56±4 MPa and E-modulus from 6±1 to...
Main Authors: | , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
International Institute for the Science of Sintering, Beograd
2004-01-01
|
Series: | Science of Sintering |
Subjects: | |
Online Access: | http://www.doiserbia.nb.rs/img/doi/0350-820X/2004/0350-820X0402087B.pdf |
id |
doaj-8f8c70c478c6444db9eb369ca4d3447b |
---|---|
record_format |
Article |
spelling |
doaj-8f8c70c478c6444db9eb369ca4d3447b2020-11-24T22:27:36ZengInternational Institute for the Science of Sintering, BeogradScience of Sintering0350-820X2004-01-01362879210.2298/SOS0402087BLiquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glassBossert J.Fidancevska E.Mangutova B.Panova B.Milosevski D.Milosevski M.Glass-ceramics were produced utilizing fly-ash from coal power stations and waste glass of TV monitors, windows and flask glass. The powder technology route was employed. The mixture of 50% fly ash and 50% waste TV glass increases the bending strength from 12±1 to 56±4 MPa and E-modulus from 6±1 to 26±3 GPa. Using polyurethane foam and C-fibers as pore creators porosity of 70±4 and 55±5 %, respectively, can be obtained-modulus and bending strength of the porous systems obtained by polyurethane foam and C-fibers was 2.7±0.5 GPa and 4.5±1 MPa and 7.1±1 GPa and 9.3±2 MPa respectively. http://www.doiserbia.nb.rs/img/doi/0350-820X/2004/0350-820X0402087B.pdfwastefly ashglass-ceramicsinteringporosity |
collection |
DOAJ |
language |
English |
format |
Article |
sources |
DOAJ |
author |
Bossert J. Fidancevska E. Mangutova B. Panova B. Milosevski D. Milosevski M. |
spellingShingle |
Bossert J. Fidancevska E. Mangutova B. Panova B. Milosevski D. Milosevski M. Liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass Science of Sintering waste fly ash glass-ceramic sintering porosity |
author_facet |
Bossert J. Fidancevska E. Mangutova B. Panova B. Milosevski D. Milosevski M. |
author_sort |
Bossert J. |
title |
Liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass |
title_short |
Liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass |
title_full |
Liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass |
title_fullStr |
Liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass |
title_full_unstemmed |
Liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass |
title_sort |
liquid phase sintering of dense and porous glass-ceramics from coal fly-ash and waste glass |
publisher |
International Institute for the Science of Sintering, Beograd |
series |
Science of Sintering |
issn |
0350-820X |
publishDate |
2004-01-01 |
description |
Glass-ceramics were produced utilizing fly-ash from coal power stations and waste glass of TV monitors, windows and flask glass. The powder technology route was employed. The mixture of 50% fly ash and 50% waste TV glass increases the bending strength from 12±1 to 56±4 MPa and E-modulus from 6±1 to 26±3 GPa. Using polyurethane foam and C-fibers as pore creators porosity of 70±4 and 55±5 %, respectively, can be obtained-modulus and bending strength of the porous systems obtained by polyurethane foam and C-fibers was 2.7±0.5 GPa and 4.5±1 MPa and 7.1±1 GPa and 9.3±2 MPa respectively. |
topic |
waste fly ash glass-ceramic sintering porosity |
url |
http://www.doiserbia.nb.rs/img/doi/0350-820X/2004/0350-820X0402087B.pdf |
work_keys_str_mv |
AT bossertj liquidphasesinteringofdenseandporousglassceramicsfromcoalflyashandwasteglass AT fidancevskae liquidphasesinteringofdenseandporousglassceramicsfromcoalflyashandwasteglass AT mangutovab liquidphasesinteringofdenseandporousglassceramicsfromcoalflyashandwasteglass AT panovab liquidphasesinteringofdenseandporousglassceramicsfromcoalflyashandwasteglass AT milosevskid liquidphasesinteringofdenseandporousglassceramicsfromcoalflyashandwasteglass AT milosevskim liquidphasesinteringofdenseandporousglassceramicsfromcoalflyashandwasteglass |
_version_ |
1725749261303283712 |