Columnar to equiaxed transition in additively manufactured CoCrFeMnNi high entropy alloy
Here, a single-track CoCrFeMnNi high entropy alloy(HEA) was prepared by laser melting deposition. The microstructural evolution of columnar to equiaxed transition was experimentally observed across the molten pool. The temperature gradient and solidification rate were theoretically calculated by a f...
Main Authors: | Hongge Li, Yongjiang Huang, Songshan Jiang, Yunzhuo Lu, Xiaoyu Gao, Xing Lu, Zhiliang Ning, Jianfei Sun |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2021-01-01
|
Series: | Materials & Design |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S0264127520307978 |
Similar Items
-
Multiphase macroscale models for macrosegregation and columnar to equiaxed transition during alloy solidification
by: Torabi Rad, Mahdi
Published: (2018) -
Microstructure formation and columnar to equiaxed transition during cold crucible directional solidification of a high-Nb TiAl alloy
by: Xuesong Xu, et al.
Published: (2021-03-01) -
The Interaction between Grains during Columnar-to-Equiaxed Transition in Laser Welding: A Phase-Field Study
by: Lingda Xiong, et al.
Published: (2020-12-01) -
Étude de la Transition Colonnaire-Equiaxe dans les lingots et en coulée continue d’acier et influence du mouvement des grains
by: Leriche, Nicolas
Published: (2015) -
Microstructure of Laser Re-Melted AlCoCrCuFeNi High Entropy Alloy Coatings Produced by Plasma Spraying
by: Haiou Yang, et al.
Published: (2013-07-01)