| Summary: | N-doped porous carbon encapsulated NiO/Ni composite nanomaterials (N-doped NiO/Ni@C) was successfully obtained by a one-step solution combustion method. This study demonstrates a one-step combustion method to synthesize n-doped porous carbon encapsulated NiO/Ni composite nanomaterials, using carbon dioxide as the carbon source, nickel nitrate as the nickel source, and hydrazine hydrate as the reaction solution. Spherical NiO nanoparticles with a particle size of 20 nm were uniformly distributed in the carbon matrix. The load of NiO/Ni can be controlled by the amount of nickel nitrate. The range of carbon content of recovered samples is 69–87 at%. The content of incorporated nitrogen for recovered samples is 1.94 at%. As the anode of lithium ion battery, the composite material exhibits high capacity, excellent multiplier performance and stable circulation performance. N-doped NiO/Ni@C-2 was applied to lithium ion batteries, and its reversible capacity maximum is 980 mAh g<sup>−1</sup> after 100 cycles at the current density of 0.1 A g<sup>−1</sup>. Its excellent electrochemical properties imply its high potential application for high-performance lithium-ion battery anode materials.
|
|---|
