Temperature dependence of the kinetics of oxygen reduction on carbon-supported Pt nanoparticles
The temperature dependence of oxygen reduction reaction (ORR) was studied on highly dispersed Pt nanoparticles supported on a carbon cryogel. The specific surface area of the support was 517 m2 g-1, the Pt particles diameter was about 2.7 nm and the loading of the catalyst was 20 wt. %. The kinetics...
Main Authors: | NEVENKA R. ELEZOVIC, BILJANA M. BABIC, NEDELJKO V. KRSTAJIC, SNEZANA LJ. GOJKOVIC, LJILJANA M. VRACAR |
---|---|
Format: | Article |
Language: | English |
Published: |
Serbian Chemical Society
2008-06-01
|
Series: | Journal of the Serbian Chemical Society |
Subjects: | |
Online Access: | http://www.shd.org.rs/JSCS/Vol73/No6/JSCS-3746.pdf |
Similar Items
-
Temperature dependence of the kinetics of oxygen reduction on carbon-supported pt nanoparticles
by: Elezović Nevenka R., et al.
Published: (2008-01-01) -
Effect of tungsten carbide in carbon Pt catalyst support on electrochemical oxygen reduction in acid solution
by: Obradović Maja D., et al.
Published: (2013-01-01) -
Characterization of a surface modified carbon cryogel and a carbon supported pt catalyst
by: Babić Biljana M., et al.
Published: (2007-01-01) -
Characterization of a surface modified carbon cryogel and a carbon supported Pt catalyst
by: BILJANA M. BABIĆ, et al.
Published: (2007-08-01) -
Tailoring Synthesis Conditions of Carbon Xerogels towards Their Utilization as Pt-Catalyst Supports for Oxygen Reduction Reaction (ORR)
by: María Jesús Lázaro, et al.
Published: (2012-10-01)