| Summary: | Al:Zr, Al-8Mg:Zr, and Al-38Mg:Zr nanocomposite particles fabricated by physical vapor deposition (PVD) and ball milling were reacted in 1 atm of pure O<sub>2</sub> within a custom, highly-sensitive micro-bomb calorimeter. The heats of combustion were compared to examine the effect of particle size and composition on combustion efficiency under room temperature and in a fixed volume. All particles yielded ~60–70% of their theoretical maximum heat of combustion and exhibited an increase in heat over composite thin films of similar compositions, which is attributed to an increase in the surface area to volume ratio. The effect of particle size and geometry are mitigated owing to the sintering of the particles within the crucible, implying the importance of particle dispersion for enhanced performance. Vaporization of the metal species may transition between two diffusion flame species (Mg to Al). As Mg content is increased, more vaporization may occur at lower temperatures, leading to an additional stage of sintering. Physically intermixed Al and Mg oxides have been observed coating the surface of the particles, which implies a continuous transition of these vaporization processes. Such nano-oxides imply high vapor-flame combustion temperatures (>2700 K) and suggest viability for agent defeat applications.
|
|---|