| Summary: | The effect of Ni-content on phase transformation behavior of NiTi-20 at. % Zr high temperature shape memory alloy (HTSMA) is investigated over a small composition range, i.e., 49.8, 50.0 and 50.2 at. % Ni, by differential scanning calorimetry (DSC), high-energy synchrotron radiation X-ray diffraction (SR-XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). All samples show a monoclinic B19′ martensitic structure at room temperature. It is shown that even with these small variations in Ni-content, the alloy shows vastly different transformation temperatures and responds in a drastically different manner to aging treatments at 550 and 600 °C. Lastly, a discussion on H-phase composition with respect to bulk composition is presented.
|
|---|