Growth, mechanical, thermal and spectral properties of Cr3+:MgMoO4 crystal.
This paper reports the growth, mechanical, thermal and spectral properties of Cr(3+):MgMoO(4) crystals. The Cr(3+):MgMoO(4) crystals with dimensions up to 30 mm×18 mm×14 mm were obtained by TSSG method. The absorption cross-sections of (4)A(2)→(4)T(1) and (4)A(2)→(4)T(2) transitions are 12.94×10(-20...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Public Library of Science (PLoS)
2012-01-01
|
| Series: | PLoS ONE |
| Online Access: | http://europepmc.org/articles/PMC3265461?pdf=render |
| Summary: | This paper reports the growth, mechanical, thermal and spectral properties of Cr(3+):MgMoO(4) crystals. The Cr(3+):MgMoO(4) crystals with dimensions up to 30 mm×18 mm×14 mm were obtained by TSSG method. The absorption cross-sections of (4)A(2)→(4)T(1) and (4)A(2)→(4)T(2) transitions are 12.94×10(-20) cm(2) at 493 nm and 7.89×10(-20) cm(2) at 705 nm for E//N(g), respectively. The Cr(3+):MgMoO(4) crystal shows broad band emission extending from 750 nm to 1300 nm with peak at about 705 nm. The emission cross-section with FWHM of 188 nm is 119.88×10(-20) cm(2) at 963 nm for E//N(g). The investigated results showed that the Cr(3+):MgMoO(4) crystal may be regarded as a potential tunable laser gain medium. |
|---|---|
| ISSN: | 1932-6203 |