Static Recrystallization Microstructure Evolution in a Cold-Deformed Ni-Based Superalloy during Electropulsing Treatment
The influence of electropulsing treatment (EPT) parameters on the static recrystallization (SRX) microstructure in a cold-deformed Ni-based superalloy was investigated. During EPT, both the volume fraction of SRX grains and the average grain size increased with the increasing EPT temperature, which...
Main Authors: | Hongbin Zhang, Chengcai Zhang, Baokun Han, Kuidong Gao, Ruirui Fang, Nana Deng, Haiping Zhou |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-09-01
|
Series: | Crystals |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4352/10/10/884 |
Similar Items
-
Evolution of grain boundary character distributions in a cold-deformed Nickel-based superalloy during electropulsing treatment
by: Hongbin Zhang, et al.
Published: (2020-05-01) -
An assessment of static recrystallization in L-605 Cobalt-based superalloy
by: Padina Ajami Ghaleh Rashidi, et al.
Published: (2016-12-01) -
Experimental and Numerical Studies on Recrystallization Behavior of Single-Crystal Ni-Base Superalloy
by: Runnan Wang, et al.
Published: (2018-07-01) -
Integrated TEM/transmission-EBSD for recrystallization analysis in nickel-based disc superalloy
by: Fei Sun
Published: (2021-02-01) -
Dynamic and Post-Dynamic Recrystallization of Haynes 282 below the Secondary Carbide Solvus
by: Emil Eriksson, et al.
Published: (2021-01-01)