Thermal fatigue cracking of die-casting dies
Die-casting dies are exposed to high thermal and mechanical loads. Thermal fatigue cracking of dies due to thermal cycling may importantly shorten the life-time of the die. Cracks degrade the surface quality of dies and consequently the surface of castings. In this study, thermal fatigue cracking of...
Main Authors: | , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Croatian Metallurgical Society
2010-01-01
|
Series: | Metalurgija |
Subjects: | |
Online Access: | http://public.carnet.hr/metalurg/Metalurgija/2010_vol_49/No_1/MET_49_1_9_12_Muhic.pdf |
Summary: | Die-casting dies are exposed to high thermal and mechanical loads. Thermal fatigue cracking of dies due to thermal cycling may importantly shorten the life-time of the die. Cracks degrade the surface quality of dies and consequently the surface of castings. In this study, thermal fatigue cracking of dies was analyzed during the process of die casting aluminium alloys. During the process cracks were observed and measured and their location and size were determined. Thermal and mechanical loads cause high local stresses and consequently surface cracks. First cracks occur as early as after 2000 cycles and propagate progressively with cycles. |
---|---|
ISSN: | 0543-5846 1334-2576 |