| Summary: | The chemical and thermal stability of zircon under low PO2 environments at different temperatures and absolute pressures have been studied. The experiments performed out in a graphite furnace at atmospheric pressure and under vacuum (1•10-3 atm) in the temperature range 1300-1500ºC up to 5 hours. Both experimental conditions and reaction mechanism were inferred from the zircon volatility diagrams, constructed as part of this work. As a result of the thermal treatments, the SiO2 was removed from the zircon, resulting in a porous layer of monoclinic zirconia with a variable thickness as a function of temperature, time and absolute pressure. A specific surface area up to 5m2/g.was obtained. This kind of materials can be used as catalyst supports in applications such as catalytic combustion and fuel cells.<br><br>Se ha estudiado el comportamiento del circón en atmósferas de baja PO2 a distintas temperaturas y presiones absolutas. Los tratamientos se han realizado en un horno de grafito a presión atmosférica y en vacío (1x10-3 atm), a temperaturas entre 1300-1500ºC, durante tiempos de hasta 5 horas. Tanto el diseño de los experimentos como la interpretación de los resultados se realizaron a partir del diagrama de volatilidad del circón, construido como parte de este trabajo. Los resultados obtenidos demuestran que en estas condiciones el circón es inestable y se reduce, perdiendo su sílice como SiO(g) y dando lugar a la formación de un recubrimiento superficial poroso de circona monoclínica, de espesor variable en función de la temperatura, tiempo y presión absoluta del tratamiento, y superficie específica comprendida entre 4 y 5m2/g. Por su microestructura y propiedades, este tipo de materiales pueden tener aplicaciones como soporte de catalizadores para combustión catalítica o en células de combustible.
|
|---|