A Novel Method for High Temperature Fatigue Testing of Nickel Superalloy Turbine Blades with Additional NDT Diagnostics
In this paper, a novel method for high temperature fatigue strength assessment of nickel superalloy turbine blades after operation at different times (303 and 473 h) was presented. The studies included destructive testing (fatigue testing at temperature 950 °C under cyclic bending load), non-destruc...
Main Authors: | Dominik Kukla, Mateusz Kopec, Ryszard Sitek, Aleksander Olejnik, Stanisław Kachel, Łukasz Kiszkowiak |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-03-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/14/6/1392 |
Similar Items
-
Fatigue crack propagation in turbine disks of EI698 superalloy
by: A.A. Shanyavskiy
Published: (2013-03-01) -
Fatigue crack propagation in turbine disks of EI698 superalloy
by: A.A. Shanyavskiy
Published: (2013-03-01) -
Restoration and Thermal Stability Investigation of Intermetllic Phase in Exposed Nickel Base Superalloy Udimet 500 Turbine Blades
by: Wangyao, P., et al.
Published: (2007-01-01) -
Electron Microscopy Characterization of the High Temperature Degradation of the Aluminide Layer on Turbine Blades Made of a Nickel Superalloy
by: Mariusz Bogdan, et al.
Published: (2020-07-01) -
Thermophysical properties of nickel-based cast superalloys
by: R. Przeliorz, et al.
Published: (2015-07-01)