Ultra-long Life Fatigue Behavior of SUJ2 Bearing Steel
Ultra-long life fatigue behavior of SUJ2 bearing steel was studied by ultrasonic fatigue testing machine. The results show that, for the crack origin of composite oxide and TiCN,crack initiates from the interface between inclusion and matrix, and for the iron-chromium carbide crack origin, the inclu...
Main Authors: | , , , |
---|---|
Format: | Article |
Language: | zho |
Published: |
Journal of Materials Engineering
2016-08-01
|
Series: | Journal of Materials Engineering |
Subjects: | |
Online Access: | http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2016.08.014 |
id |
doaj-be28c9c719384b4fb36fe522a475da91 |
---|---|
record_format |
Article |
spelling |
doaj-be28c9c719384b4fb36fe522a475da912020-11-24T23:03:20ZzhoJournal of Materials EngineeringJournal of Materials Engineering1001-43811001-43812016-08-01448859210.11868/j.issn.1001-4381.2016.08.01420160814Ultra-long Life Fatigue Behavior of SUJ2 Bearing SteelLI Yong-de0ZHANG Li-li1ZHANG Chong2HE Ying-ying3Equipment Manufacturing College, Hebei University of Engineering, Handan 056038, Hebei, ChinaEquipment Manufacturing College, Hebei University of Engineering, Handan 056038, Hebei, ChinaShandong Analysis and Test Center, Jinan 250014, ChinaJiangsu Iron & Steel Research Institute(Shagang), Zhangjiagang 215625, Jiangsu, ChinaUltra-long life fatigue behavior of SUJ2 bearing steel was studied by ultrasonic fatigue testing machine. The results show that, for the crack origin of composite oxide and TiCN,crack initiates from the interface between inclusion and matrix, and for the iron-chromium carbide crack origin, the inclusion itself cracks. The relative GBF(granular bright facet) size is proportional to 1/Δ<i>K</i><sub>inc</sub><sup>2</sup>. GBF is no longer formed when Δ<i>K</i><sub>inc</sub>>8MPa·m<sup>1/2</sup> for SUJ2 bearing steel. The crack propagation rule in GBF is obtained by data fitting, it is verified that Paris equation which can describe the crack growth in GBF is verified.http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2016.08.014ultra-long life fatigueinclusionrelative GBF sizecrack propagation |
collection |
DOAJ |
language |
zho |
format |
Article |
sources |
DOAJ |
author |
LI Yong-de ZHANG Li-li ZHANG Chong HE Ying-ying |
spellingShingle |
LI Yong-de ZHANG Li-li ZHANG Chong HE Ying-ying Ultra-long Life Fatigue Behavior of SUJ2 Bearing Steel Journal of Materials Engineering ultra-long life fatigue inclusion relative GBF size crack propagation |
author_facet |
LI Yong-de ZHANG Li-li ZHANG Chong HE Ying-ying |
author_sort |
LI Yong-de |
title |
Ultra-long Life Fatigue Behavior of SUJ2 Bearing Steel |
title_short |
Ultra-long Life Fatigue Behavior of SUJ2 Bearing Steel |
title_full |
Ultra-long Life Fatigue Behavior of SUJ2 Bearing Steel |
title_fullStr |
Ultra-long Life Fatigue Behavior of SUJ2 Bearing Steel |
title_full_unstemmed |
Ultra-long Life Fatigue Behavior of SUJ2 Bearing Steel |
title_sort |
ultra-long life fatigue behavior of suj2 bearing steel |
publisher |
Journal of Materials Engineering |
series |
Journal of Materials Engineering |
issn |
1001-4381 1001-4381 |
publishDate |
2016-08-01 |
description |
Ultra-long life fatigue behavior of SUJ2 bearing steel was studied by ultrasonic fatigue testing machine. The results show that, for the crack origin of composite oxide and TiCN,crack initiates from the interface between inclusion and matrix, and for the iron-chromium carbide crack origin, the inclusion itself cracks. The relative GBF(granular bright facet) size is proportional to 1/Δ<i>K</i><sub>inc</sub><sup>2</sup>. GBF is no longer formed when Δ<i>K</i><sub>inc</sub>>8MPa·m<sup>1/2</sup> for SUJ2 bearing steel. The crack propagation rule in GBF is obtained by data fitting, it is verified that Paris equation which can describe the crack growth in GBF is verified. |
topic |
ultra-long life fatigue inclusion relative GBF size crack propagation |
url |
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2016.08.014 |
work_keys_str_mv |
AT liyongde ultralonglifefatiguebehaviorofsuj2bearingsteel AT zhanglili ultralonglifefatiguebehaviorofsuj2bearingsteel AT zhangchong ultralonglifefatiguebehaviorofsuj2bearingsteel AT heyingying ultralonglifefatiguebehaviorofsuj2bearingsteel |
_version_ |
1725634300281356288 |