| Summary: | Stone matrix asphalt (SMA) mixtures are one of the most resistant types of asphalt mixtures known to date that the bulk load is borne by the aggregate skeleton. In this research, the effect of crumb rubber powder (CRP), Vestenamer polymer, and warm additives, including Sasobit, ZycoTherm, and a porous and warm mix asphalt (PAWMA), was investigated on the moisture resistance of SMA mixtures. A segregation test was performed to determine the tendency of the polymer to separate from modified polymer bitumen under storage conditions. Also, a drain down sensitivity test was conducted to explore the bleeding phenomena and drain down of SMA mixtures. Finally, a boiling water test, as well as an indirect tensile strength (ITS) test, was applied to examine the sensitivity of mixtures to moisture. The segregation test results indicated that by the use of Vestenamer polymer, a conventional (low speed) mixer can be used instead of using a high-speed mixer, and this will be very important in the cost of rubber bitumen production. The drain down test results showed that cellulose fibers prevented the bitumen bleeding of SMA mixtures. Also, the results of the boiling water test indicated that CRP samples containing ZycoTherm had the highest moisture resistance compared to the other warm additives. Among various mixtures, 8% CRP-modified samples containing ZycoTherm resulted in the lowest amount of stripping in SMA mixtures, even more than the base sample. The ITS test results illustrated that the use of CRP, Vestenamer polymer, and warm additives had a significant effect on the ITS amounts of mixtures. Moreover, the samples containing ZycoTherm had the highest tensile strength ratio (TSR) compared to the other SMA samples.
|
|---|