Abnormal grain growth in thin wires of commercially pure iron with anisotropic microstructure
This work reports the behavior of annealed commercially pure cold-drawn thin iron wires. Primary recrystallization is complete after holding for 180 s at 1123 K. After recrystallization, grain growth takes place within the central region but not close to the surface. For annealing times up to 14400 ...
Main Authors: | D.R. Almeida Jr., P.R. Rios, D. Zöllner, H.R.Z. Sandim |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2020-09-01
|
Series: | Journal of Materials Research and Technology |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2238785420315635 |
Similar Items
-
Evolution of Recrystallized Grain and Texture of Cold-Drawn Pure Mg Wire and Their Effect on Mechanical Properties
by: Jiao Meng, et al.
Published: (2020-01-01) -
Fabrication of 50.0 μm Ultra-Fine Pure Rhodium Wire, Using a Multi-Pass Wire Drawing Process, for Probe Card Pins
by: Sang-Kon Lee, et al.
Published: (2019-07-01) -
WIRE BREAKAGE DURING WIRE DRAWING DUE TO THE PRESENCE OF SURFACE DEFECTS, INHERITED FROM WIRE ROD
by: A. S. Siarohina
Published: (2018-01-01) -
On Pin-to-wire Routing in FPGAs
by: Shah, Niyati
Published: (2012) -
On Pin-to-wire Routing in FPGAs
by: Shah, Niyati
Published: (2012)