Microstructure and microhardness of Ti-48Al alloy prepared by rapid solidification
To improve the microstructure and microhardness, Ti-48Al (at.%) alloy was rapidly solidified by melt spinning under different cooling rates. The microstructure and microhardness of rapidly solidified Ti-48Al alloy were systematically investigated. Results show that the average lamellar colony size o...
Main Authors: | Xiao-yu Chen, Hong-ze Fang, Qi Wang |
---|---|
Format: | Article |
Language: | English |
Published: |
Foundry Journal Agency
2020-11-01
|
Series: | China Foundry |
Subjects: | |
Online Access: | https://link.springer.com/article/10.1007/s41230-020-0090-7 |
Similar Items
-
Dependency of microstructure and microhardness on withdrawal rate of Ti-43Al-2Cr-2Nb alloy prepared by electromagnetic cold crucible directional solidification
by: Yong-zhe Wang, et al.
Published: (2016-07-01) -
Rapid Cooling and Solidification Microstructure of Argon Atomized Ti-48Al Alloy Droplets
by: BAO Ying, et al.
Published: (2018-12-01) -
The Directional Solidification, Microstructural Characterization and Deformation Behavior of β-Solidifying TiAl Alloy
by: Ning Cui, et al.
Published: (2019-04-01) -
Microstructures, micro-segregation and solidification path of directionally solidified Ti-45Al-5Nb alloy
by: Liang-shun Luo, et al.
Published: (2016-03-01) -
Effects of Thermal Variables of Solidification on the Microstructure, Hardness, and Microhardness of Cu-Al-Ni-Fe Alloys
by: Maurício Silva Nascimento, et al.
Published: (2019-04-01)