Deuterium retention behavior in simultaneously He+–D2+ implanted tungsten
Poly-crystalline tungsten (W) samples were simultaneously irradiated with Helium (He) and Deuterium (D) ions using the triple-ion implantation device. He effect on D retention and transportation was studied using different combination of ion energies and He/D flux ratios in the simultaneous implanta...
Main Authors: | Qilai Zhou, Keisuke Azuma, Akihiro Togari, Miyuki Yajima, Masayuki Tokitani, Suguru Masuzaki, Naoaki Yoshida, Masanori Hara, Yuji Hatano, Yasuhisa Oya |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2018-08-01
|
Series: | Nuclear Materials and Energy |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2352179117301606 |
Similar Items
-
Surface or bulk He existence effect on deuterium retention in Fe ion damaged W
by: Yasuhisa Oya, et al.
Published: (2018-08-01) -
Kinetics of deuterium penetration into neutron-irradiated tungsten under exposure to high flux deuterium plasma
by: M. Yajima, et al.
Published: (2019-12-01) -
Effect of periodic deuterium ion irradiation on deuterium retention and blistering in Tungsten
by: M. Oya, et al.
Published: (2017-08-01) -
Influence of thermal shocks on the He induced surface morphology on tungsten
by: Y. Hamaji, et al.
Published: (2019-01-01) -
Damage and deuterium retention of re-solidified tungsten following vertical displacement event-like heat load
by: Y. Hamaji, et al.
Published: (2017-08-01)