Microstructure and Properties of Mechanical Alloying Al-Zr Coating by High Current Pulsed Electron Beam Irradiation
The "HOPE-I" type high-current pulsed electron beam (HCPEB) equipment was used to irradiate the pure aluminum material with Zr coating preset by ball milling to realize the alloying of a Zr–Al coating surface. The microstructure and phase analysis were conducted by XRD, SEM, and TEM. The e...
Main Authors: | Xiangcheng Li, Huiru Liu, Nana Tian, Conglin Zhang, Peng Lyu, Qingfeng Guan |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-11-01
|
Series: | Nanomaterials |
Subjects: | |
Online Access: | https://www.mdpi.com/2079-4991/10/12/2398 |
Similar Items
-
Crater Formation on the Surface of Pure Metal and Alloy Irradiated by High Current Pulsed Electron Beam
by: Cai Jie, et al.
Published: (2018-08-01) -
Nanocrystalline Cr-Ni Alloying Layer Induced by High-Current Pulsed Electron Beam
by: Lingyan Zhang, et al.
Published: (2019-01-01) -
Microstructure and property modifications in surface layers of a Mg-4Sm-2Al-0.5Mn alloy induced by pulsed electron beam treatments
by: Yingrui Liu, et al.
Published: (2021-01-01) -
Study on microstructure and wear resistance of Zr-17Nb alloy irradiated by high current pulsed electron beam
by: Sun Yue, et al.
Published: (2020-11-01) -
Fibrous nano composite reinforced surface on WC-Co cemented carbide achieved by pulsed electron beam irradiation and subsequent tempering
by: Peng Wenhai, et al.
Published: (2021-01-01)