| Summary: | <b> </b>This study successfully fabricated BPA-imprinted poly(4-vinylpyridine-co-ethylene glycol dimethacrylate) (poly(4-VP-co-EGDMA)) quartz crystal microbalance (MIP-QCM) sensors on a silica skeleton surface and gold pinholes of silica inverse opal through surface-initiated atom transfer radical polymerization (SI-ATRP). The sensing features of the two MIP films on the structured silica surface and nano-scale local gold surface were investigated by measuring the resonant frequency change (<i>f</i>) in QCM sensors. The <i>f</i> values for the <i>p</i>-MIP (MIP on gold pinholes) and <i>s</i>-MIP films (MIP on silica skeleton surface) were obtained with the <i>f</i> value of −199 4.9 Hz and −376 19.1 Hz, respectively, whereas for <i>p</i>-/<i>s</i>-NIP films, the <i>f</i> values were observed to be −115 19.2 Hz and −174 5.8 Hz by the influence of non-specific adsorption on the surface of the films. Additionally, the imprinting factor (IF) appeared to be 1.72 for <i>p</i>-MIP film and 2.15 for <i>s</i>-MIP film, and the limits of quantitation (LOQ) and detection (LOD) were 54.924 and 18.125 nM (<i>p</i>-MIP film) and 38.419 and 12.678 nM (<i>s</i>-MIP film), respectively. Using the Freundlich isotherm model, the binding affinity of the BPA-imprinted films was evaluated. This was measured in an aqueous solution of BPA whose concentration ranged between 45 and 225 nM. It was found that the <i>p</i>-MIP film (m = 0.39) was relatively more heterogeneous than the <i>s</i>-MIP film (m = 0.33), both of which were obtained from the slope of the linear regressions. Finally, the selectivity of the MIP-QCM sensors for BPA detection was determined by measuring the effect of other analogous chemicals, such as bisphenol F (BPF), bisphenol AP (BPAP), and bisphenol B (BPB), in aqueous solutions. The selectivity coefficients (<i>k</i>*) of the two MIP films had ~1.9 for the <i>p</i>-MIP and ~2.3 for the <i>s</i>-MIP films, respectively. The results reveal that, with respect to signal amplification of the QCM sensors, the s-MIP film has better sensing features and faster detection responses than the <i>p</i>-MIP film.
|
|---|