Comparison of the Dislocation Structure of a CrMnN and a CrNi Austenite after Cyclic Deformation

In the literature, the effects of nitrogen on the strength of austenitic stainless steels as well as on cold deformation are well documented. However, the effect of N on fatigue behaviour is still an open issue, especially when comparing the two alloying concepts for austenitic stainless steels&...

Full description

Bibliographic Details
Main Authors: Rainer Fluch, Marianne Kapp, Krystina Spiradek-Hahn, Manfred Brabetz, Heinz Holzer, Reinhard Pippan
Format: Article
Language:English
Published: MDPI AG 2019-07-01
Series:Metals
Subjects:
Online Access:https://www.mdpi.com/2075-4701/9/7/784
Description
Summary:In the literature, the effects of nitrogen on the strength of austenitic stainless steels as well as on cold deformation are well documented. However, the effect of N on fatigue behaviour is still an open issue, especially when comparing the two alloying concepts for austenitic stainless steels—CrNi and CrMnN—where the microstructures show a different evolution during cyclic deformation. In the present investigation, a representative sample of each alloying concept has been tested in a resonant testing machine at ambient temperature and under stress control single step tests with a stress ratio of 0.05. The following comparative analysis of the microstructures showed a preferred formation of cellular dislocation substructures in the case of the CrNi alloy and distinct planar dislocation glide in the CrMnN steel, also called high nitrogen steel (HNS). The discussion of these findings deals with potential explanations for the dislocation glide mechanism, the role of N on this phenomenon, and the consequences on fatigue behaviour.