INFLUENCE OF MANGANESE ON THE SINTERING PROPERTIES OF TETRAGONAL ZIRCONIA
The influence of small additions of MnO2 (up to 1 wt. %) on the sintering behaviour of yttria-stabilized zirconia sintered over the temperature range from 1250°C to 1500°C was investigated. It was found that the mechanical properties of Y-TZP were dependent on the dopant amount and sintering tempera...
Main Authors: | , , , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
University of Chemistry and Technology, Prague
2013-03-01
|
Series: | Ceramics-Silikáty |
Subjects: | |
Online Access: | http://www.ceramics-silikaty.cz/2013/pdf/2013_01_028.pdf |
Summary: | The influence of small additions of MnO2 (up to 1 wt. %) on the sintering behaviour of yttria-stabilized zirconia sintered over the temperature range from 1250°C to 1500°C was investigated. It was found that the mechanical properties of Y-TZP were dependent on the dopant amount and sintering temperature. The results revealed that relative densities above 97.5 % of theoretical (i.e. > 5.95 Mg m-3) could be obtained in Y-TZPs sintered at low temperatures, 1250°C and 1300°C, with the additions of ≥ 0.3 wt. % MnO2. In comparison to the undoped samples, the additions of up to 1 wt. % MnO2 and for sintering up to 1350°C was found to be beneficial in enhancing the Vickers hardness of the ceramic. The fracture toughness of Y-TZP however, was found to increase only in the 1 wt. % MnO2-doped samples when sintered above 1400°C. The relation between the measured mechanical properties is discussed with the emphasis on the role of the manganese oxide. |
---|---|
ISSN: | 0862-5468 1804-5847 |