STATISTIC METHODS OF POLYIMIDE ENAMEL ISOLATION DEFECTIVE NON-DESTRUCTIVE CONTROL AT THE CONDITIONS OF PRODUCTION
In this paper can be used to not-destructive technological testing of defects isolation enameled wire with polyimide polymer. The thesis is devoted to the statistical method for processing, comparison and analysis of results of measurements of parameters isolation it enameled wire because of mathema...
Main Authors: | , |
---|---|
Format: | Article |
Language: | English |
Published: |
National Technical University "Kharkiv Polytechnic Institute"
2017-03-01
|
Series: | Електротехніка і електромеханіка |
Subjects: | |
Online Access: | http://eie.khpi.edu.ua/article/view/2074-272X.2017.1.08/89722 |
Summary: | In this paper can be used to not-destructive technological testing of defects isolation enameled wire with polyimide polymer. The thesis is devoted to the statistical method for processing, comparison and analysis of results of measurements of parameters isolation it enameled wire because of mathematical model of trend for application in active technological monitoring is developed; to development used of the recommendations for parameters of such testing. Is theoretically justified and the possibility of a diminution of dependence of an error from a velocity of movement of a wire for want of quantifying of defects enameled isolation not destroying tests by high voltage. This work is devoted to the statistical method for processing, comparison and analysis of results of measurements of parameters of polyimide isolation. The method is operating not destroying technological monitoring an amount of enameled isolation defect. The dependence of average value of amount of defects for enameled wire ПЭЭИДХ2 – 200 with two–sheeted polyimide by isolation in a range of nominal diameter 0.56 mm is experimentally determined. The technological monitoring purpose is reducing of quantifying of enameled isolation defect. |
---|---|
ISSN: | 2074-272X 2309-3404 |