Effect of the PEN/C surface layer modification on the microstructure, mechanical and tribological properties of the 30CrMnSiA mild-carbon steel
As result of plasma-electrolytic nitrocarburizing 30CrMnSiA carbon steel (ferrite-perlite grade), there was a change in the elemental and phase composition, as well as the surface layer microstructure (40 ÷ 45 microns thick from the surface). A formation of Me23(CN)6 carbonitrides, FeN nitrides, Fe3...
Main Authors: | L.G. Zhurerova, B.K. Rakhadilov, N.A. Popova, M.K. Kylyshkanov, V.V. Buranich, A.D. Pogrebnjak |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2020-01-01
|
Series: | Journal of Materials Research and Technology |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2238785419305927 |
Similar Items
-
Effect of Loading Frequency Ratio on Multiaxial Asynchronous Fatigue Failure of 30CrMnSiA Steel
by: Tianqi Liu, et al.
Published: (2021-07-01) -
Effect of Phase Angle on Fatigue Failure of 30CrMnSiA Steel under Tension-torsion Fatigue Loading
by: Liu Tianqi, et al.
Published: (2016-01-01) -
The cathodic electrolytic plasma hardening of the 20Cr2Ni4A chromium-nickel steel
by: Bauyrzhan K. Rakhadilov, et al.
Published: (2020-07-01) -
Structure and Tribological Properties of Ni–Cr–Al-Based Gradient Coating Prepared by Detonation Spraying
by: Bauyrzhan Rakhadilov, et al.
Published: (2021-02-01) -
Change of 0.34Cr-1Ni-Mo-Fe Steel Dislocation Structure in Plasma Electrolyte Hardening
by: Bauyrzhan Rakhadilov, et al.
Published: (2021-04-01)