A superior strength and sliding-wear resistance combination of ductile iron with nanobainitic matrix
A nanobainitic matrix composing of nanoscale α phase and carbon-riched γ phase was obtained for the ductile iron by austempering treatment. The microstructure and properties of ductile iron were compared with GCr15. The microstructural characteristic gave rise to a good strength with an ultimate ten...
Main Authors: | Yuzhou Du, Xiaolong Wang, Dongya Zhang, Xin Wang, Chunpeng Ju, Bailing Jiang |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2021-03-01
|
Series: | Journal of Materials Research and Technology |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2238785421001046 |
Similar Items
-
Effect of Nanobainite Content on the Dry Sliding Wear Behavior of an Al-Alloyed High Carbon Steel with Nanobainitic Microstructure
by: Zhaohuan Song, et al.
Published: (2019-05-01) -
Corrosion Resistance of The Bearing Steel 67SiMnCr6-6-4 with Nanobainitic Structure
by: Skołek E., et al.
Published: (2015-04-01) -
Wear behavior of nanostructured carbo-austempered cast steels under rolling-sliding conditions
by: Oscar Ríos-Diez, et al.
Published: (2021-03-01) -
Wear Behavior of Austempered Ductile Iron with Nanosized Additives
by: J. Kaleicheva
Published: (2014-03-01) -
Effect of Phenomena Accompanying Wear in Dry Corundum Abrasive on the Properties and Microstructure of Austempered Ductile Iron with Different Chemical Composition
by: Myszka D., et al.
Published: (2015-04-01)