Si-TCP synthesized from "Mg-free" reagents employed as calcium phosphate cement
The influence of silicon doping on calcium phosphate cement were explored in this work. α-TCP and Si-α-TCP were prepared by solid state reaction employing "Mg-free" CaHPO4, CaCO3 and CaSiO3 as precursors. It was possible to obtain TCP powders with low contents of ^...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2012-08-01
|
| Series: | Materials Research |
| Subjects: | |
| Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392012000400014 |
| Summary: | The influence of silicon doping on calcium phosphate cement were explored in this work. α-TCP and Si-α-TCP were prepared by solid state reaction employing "Mg-free" CaHPO4, CaCO3 and CaSiO3 as precursors. It was possible to obtain TCP powders with low contents of β phase as contaminant. Cement liquid phase was an aqueous solution containing 2.5 wt. (%) of Na2HPO4 and 1.5 wt. (%) of citric acid. The liquid-to-powder ratio was 0.6 mL.g-1. Chemical, physical and mechanical properties of the cement samples were determined by means of XRD, FTIR, XRF, compressive strength and SEM. The calcium phosphate cements obtained achieved satisfactory properties; however, Si-α-TCP presented a decrease on the rate of setting reaction. |
|---|---|