Study on the Influence of AC Stray Current on X80 Steel under Stripped Coating by Electrochemical Method
The effect of AC stray current density on corrosion behavior of X80 steel with stripped coating defects was studied by electrochemical method. The experimental results showed that the open circuit potential of X80 steel was shifted negatively due to the existence of AC interference. The degree of ne...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2019-01-01
|
| Series: | International Journal of Corrosion |
| Online Access: | http://dx.doi.org/10.1155/2019/4372430 |
| Summary: | The effect of AC stray current density on corrosion behavior of X80 steel with stripped coating defects was studied by electrochemical method. The experimental results showed that the open circuit potential of X80 steel was shifted negatively due to the existence of AC interference. The degree of negative shift increased with the increasing of AC stray current density. And the potential after the cut of AC interference was still more negative than before. That is, the corrosion interference continued after cutting the AC power. In the initial stage of the experiment, the corrosion current density with 30A/m2 AC stray current interference was about 1.4 times of that without AC interference, while the corrosion current density with 50A/m2 AC stray current interference was about two times of that without AC interference. |
|---|---|
| ISSN: | 1687-9325 1687-9333 |