Effects of the atmosphere and substrate on the crystallization of PLZT thin films
Lead lanthanum zirconate titanate [PLZT (9/65/35)] thin films were prepared by dip-coating on Si (100) or Si/Ti/Pt (100) substrates using a polymeric precursor solution and annealed at 650 °C for 3 h. Perovskite phase formation of the PLZT thin films and microstructure were analysed using XRD and SE...
Main Authors: | , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2000-07-01
|
Series: | Materials Research |
Subjects: | |
Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392000000300004 |
Summary: | Lead lanthanum zirconate titanate [PLZT (9/65/35)] thin films were prepared by dip-coating on Si (100) or Si/Ti/Pt (100) substrates using a polymeric precursor solution and annealed at 650 °C for 3 h. Perovskite phase formation of the PLZT thin films and microstructure were analysed using XRD and SEM. Effects of Si (100), Si/Ti/Pt (100) substrates and atmosphere on crystallization of PLZT thin films were studied. Films deposited on platinum coated silicon (100) show a heterogeneous surface with presence of bubbles. Otherwise, the PLZT (9/65/35) thin films deposited on silicon (100) substrate shows a more uniform surface after annealing in oxygen atmosphere. |
---|---|