Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing Environment
The effect of high temperature on corrosion behavior and passive film composition of Ni-based alloy 825 in H2S-containing environment was investigated by Confocal Laser Microscope (CLM), Scanning Electron Microscope (SEM), Energy Dispersive Spectrometer (EDS), and X-ray Photoelectron Spectroscopy (X...
Main Authors: | , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Frontiers Media S.A.
2021-09-01
|
Series: | Frontiers in Materials |
Subjects: | |
Online Access: | https://www.frontiersin.org/articles/10.3389/fmats.2021.728898/full |
id |
doaj-e6a9b05e77a8411bba4988828543bc4b |
---|---|
record_format |
Article |
spelling |
doaj-e6a9b05e77a8411bba4988828543bc4b2021-09-07T05:56:53ZengFrontiers Media S.A.Frontiers in Materials2296-80162021-09-01810.3389/fmats.2021.728898728898Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing EnvironmentZhe Feng0Xuehua Fan1Zhu Wang2Yong Yu3Lijuan Chen4Yanxia Du5Lei Dong6Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing, ChinaChina Petroleum Engineering and Construction Co., Ltd. Beijing Company, Beijing, ChinaInstitute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing, ChinaChina Petroleum Engineering and Construction Co., Ltd. Beijing Company, Beijing, ChinaChina Petroleum Engineering and Construction Co., Ltd. Beijing Company, Beijing, ChinaInstitute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing, ChinaChina Petroleum Engineering and Construction Co., Ltd. Beijing Company, Beijing, ChinaThe effect of high temperature on corrosion behavior and passive film composition of Ni-based alloy 825 in H2S-containing environment was investigated by Confocal Laser Microscope (CLM), Scanning Electron Microscope (SEM), Energy Dispersive Spectrometer (EDS), and X-ray Photoelectron Spectroscopy (XPS). The experiment was carried out at 150 and 230°C in NaCl solution. The partial pressure of H2S was set to 1.2 MPa and CO2 was set to 3.2 MPa. The results showed that Ni-based alloy 825 presented good general corrosion resistance. Pitting corrosion was likely to occur at 230°C because of Cr depleted in the passive film. NiS appeared at high temperature and is damaging to protectiveness of passive film.https://www.frontiersin.org/articles/10.3389/fmats.2021.728898/fullnickel based alloyhydrogen sulfidepittingpassive filmhigh temperature |
collection |
DOAJ |
language |
English |
format |
Article |
sources |
DOAJ |
author |
Zhe Feng Xuehua Fan Zhu Wang Yong Yu Lijuan Chen Yanxia Du Lei Dong |
spellingShingle |
Zhe Feng Xuehua Fan Zhu Wang Yong Yu Lijuan Chen Yanxia Du Lei Dong Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing Environment Frontiers in Materials nickel based alloy hydrogen sulfide pitting passive film high temperature |
author_facet |
Zhe Feng Xuehua Fan Zhu Wang Yong Yu Lijuan Chen Yanxia Du Lei Dong |
author_sort |
Zhe Feng |
title |
Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing Environment |
title_short |
Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing Environment |
title_full |
Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing Environment |
title_fullStr |
Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing Environment |
title_full_unstemmed |
Corrosion Behavior and Passive Film Composition of Alloy 825 in High Temperature and High H2S-CO2 Containing Environment |
title_sort |
corrosion behavior and passive film composition of alloy 825 in high temperature and high h2s-co2 containing environment |
publisher |
Frontiers Media S.A. |
series |
Frontiers in Materials |
issn |
2296-8016 |
publishDate |
2021-09-01 |
description |
The effect of high temperature on corrosion behavior and passive film composition of Ni-based alloy 825 in H2S-containing environment was investigated by Confocal Laser Microscope (CLM), Scanning Electron Microscope (SEM), Energy Dispersive Spectrometer (EDS), and X-ray Photoelectron Spectroscopy (XPS). The experiment was carried out at 150 and 230°C in NaCl solution. The partial pressure of H2S was set to 1.2 MPa and CO2 was set to 3.2 MPa. The results showed that Ni-based alloy 825 presented good general corrosion resistance. Pitting corrosion was likely to occur at 230°C because of Cr depleted in the passive film. NiS appeared at high temperature and is damaging to protectiveness of passive film. |
topic |
nickel based alloy hydrogen sulfide pitting passive film high temperature |
url |
https://www.frontiersin.org/articles/10.3389/fmats.2021.728898/full |
work_keys_str_mv |
AT zhefeng corrosionbehaviorandpassivefilmcompositionofalloy825inhightemperatureandhighh2sco2containingenvironment AT xuehuafan corrosionbehaviorandpassivefilmcompositionofalloy825inhightemperatureandhighh2sco2containingenvironment AT zhuwang corrosionbehaviorandpassivefilmcompositionofalloy825inhightemperatureandhighh2sco2containingenvironment AT yongyu corrosionbehaviorandpassivefilmcompositionofalloy825inhightemperatureandhighh2sco2containingenvironment AT lijuanchen corrosionbehaviorandpassivefilmcompositionofalloy825inhightemperatureandhighh2sco2containingenvironment AT yanxiadu corrosionbehaviorandpassivefilmcompositionofalloy825inhightemperatureandhighh2sco2containingenvironment AT leidong corrosionbehaviorandpassivefilmcompositionofalloy825inhightemperatureandhighh2sco2containingenvironment |
_version_ |
1717764848664707072 |