Study of short cracks under biaxial fatigue
In this paper a methodology for evaluating crack initiation under biaxial conditions is presented. The methodology consists of evaluating the crack length automatically with digital processing of highmagnification images of the crack. The methodology was applied to study five different strain cond...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2014-10-01
|
| Series: | Frattura ed Integrità Strutturale |
| Subjects: | |
| Online Access: | http://www.gruppofrattura.it/pdf/rivista/numero30/numero_30_art_31.pdf |
| Summary: | In this paper a methodology for evaluating crack initiation under biaxial conditions is presented.
The methodology consists of evaluating the crack length automatically with digital processing of highmagnification
images of the crack. The methodology was applied to study five different strain conditions on a
low carbon ferritic-pearlitic steel specimen with tubular shape. A hole of 150 μm diameter was drilled to enforce
the crack to initiate at a particular spot. Different combinations of axial and torsional strains were analysed
during the initiation stage of the crack. The setup employed allowed detection of the crack to within 6 μm from
the edge of the hole on average and monitoring of the crack during early stages. Fatigue crack propagation
curves clearly showed oscillations due to microstructure. It was also observed that these oscillations decreased
as the torsional component of the strain was increased. |
|---|---|