^1H NMR tests on damaged and undamaged XLPE and SiR samples

^1H NMR tests on damaged and undamaged XLPE and SiR samples

Cross-linked polyethylene (XLPE) and silicone rubber (SiR) samples were subjected to a high-voltage AC stress plane–plane configuration and inclined plane test, respectively. The voltage was applied such that discharge was observed across the surface of the XLPE test sample for several hours and for...

Full description

Bibliographic Details
Main Authors: Lydia Gkoura, Taiji Wang, Athanasios Anastasiou, Noureddine Harid, Huw Griffiths, Manu Haddad, Michalis Fardis, Marina Karayianni
Format: Article
Language:English
Published: Wiley 2019-07-01
Series:High Voltage
Subjects:
silicone rubber
bonds (chemical)
XLPE insulation
nuclear spin-lattice relaxation
proton magnetic resonance
spin-spin relaxation
discharges (electric)
undamaged XLPE
SiR samples
damaged samples
damaged XLPE
inclined plane test
XLPE test sample
visible damage
virgin samples
nuclear magnetic resonance spectroscopy
stressed samples
^1H NMR tests
high-voltage AC stress plane-plane configuration
cross-linked polyethylene
silicone rubber samples
discharge
^1H NMR spin-lattice relaxation time measurements
^1H NMR spin-spin relaxation time measurements
chemical bonding
Online Access:https://digital-library.theiet.org/content/journals/10.1049/hve.2019.0077

Internet

https://digital-library.theiet.org/content/journals/10.1049/hve.2019.0077