Ply cracking and stiffness degradation in cross-ply laminates under biaxial extension, bending and thermal loading
Transverse ply cracking often leads to the loss of stiffness and reduction in thermal expansion coefficients. This paper presents the thermoelastic degradation of general cross-ply laminates, containing transverse ply cracks, subjected to biaxial extension, bending and thermal loading. The stress an...
Main Authors: | Lam, Dennis, Zhang, D., Ye, J. |
---|---|
Language: | en |
Published: |
2013
|
Subjects: | |
Online Access: | http://hdl.handle.net/10454/5555 |
Similar Items
-
Ply cracking and stiffness degradation in cross-ply laminates under biaxial extension, bending and thermal loading.
by: Zhang, D., et al.
Published: (2014) -
Fatigue crack initiation in cross-ply carbon fiber laminates
by: Ketterer, Justin M.
Published: (2009) -
Free-Edge and Ply Cracking Effect in Angle-Ply Laminated Composites Subjected to In-Plane Loads.
by: Zhang, D., et al.
Published: (2014) -
Estimate of compressive strength of an unidirectional composite lamina using cross-ply and angle-ply laminates
by: M. Scafè, et al.
Published: (2014-07-01) -
Effect of Off-Axis Ply on Tensile Properties of [0/θ]<sub>ns</sub> Thin Ply Laminates by Experiments and Numerical Method
by: Junfeng Hu, et al.
Published: (2021-05-01)