Previous issue date: 2017-09-14 === Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) === O niobato de ferro (FeNbO4) tem sido aplicado como foto?nodo em conversores de energia solar, sensores a g?s, tecnologias catal?ticas, fotodectoras e dispositivos eletr?nicos. No entanto, as descri??es de suas propriedades diel?tricas ainda s?o muito escassas. Foi preparado tr?s tipos de amostras a partir da moagem de alta energia (24h, 48h e 72h) dos precursores de: Nb2O5, ?-Fe e H2O. Depois do processo de moagem, os p?s resultantes da moagem passaram pelo processo de calcina??o por 4 horas a 1300?C. O tempo de calcina??o foi o mesmo para todas. Todas essas amostras passaram pela caracteriza??o diel?trica, mas antes elas foram prensadas a 1570 Kgf e sinterizadas ? 1000_C por 24 horas. As caracteriza??es estruturais das amostras foram realizadas atrav?s da difra??o de raios X, microscopia eletr?nica de varredura e fluoresc?ncia de raios X. Os resultados revelaram que a amostra mo?da por 24h tem 94,48 % de FeNbO4 e 5,52 % de Fe2O3, para 48h tem 97,82 % de FeNbO4 e 2,18 % de Fe2O3, para 72h tem 93,68 % de FeNbO4 e 6,32 % de Fe2O3. As propriedades diel?tricas foram analisadas atrav?s das curvas caracter?sticas I-V e da permissividade diel?trica complexa com rela??o a frequ?ncia. As curvas caracter?sticas obtidas mostraram um comportamento semelhante a dispositivos eletr?nicos semicondutores, pertencente a fam?lia dos tiristores. O nosso estudo trata de uma nova rota de s?ntese para obten??o do niobato de ferro. Os resultados indicam que as amostras t?m grande potencial para aplica??o em dispositivos eletr?nicos. === Iron niobate (FeNbO4) has been applied to the photodiode in solar energy converters,
gas sensors, photo detectors, and electronic devices. However, a full description of your
dielectric properties is still scarceness so. By using a high energy mill, they were prepared
three kinds of samples (24, 48 and 72 hours) of the precursors of: Nb2O5, a-Fe e H2O.
After milling process, the resultant powders were to calcinated for precisely 4 hours and
in a temperature of 1 300 celsius. We used a hydraulic press about 1570 Kgf to produce
the samples. Next, the samples were calcinated during a time considered the same for
all of them and underwent to dielectric characterization. In the way to characterize the
samples, the samples were submitted to X rays, scanning electronic microscopy and X
rays
uorescence. Results have been shown that samples milling by 24 hours, has 94.48%
of FeNbO4 and 5.52% of Fe2O3, by 48h has 97.82% of FeNbO4 and 2,18% de Fe2O3, and
by 72h has 93,68% of FeNbO4 and 6.32% of Fe2O3. Dielectric properties were analyzed
through I-V characteristic curves and complex dielectric permitivity against frequency.
The characteristic curves exhibited semiconductors electronic devices behave like thyristor
class. Furthermore, the present work constitutes a fully new route to sintering iron
niobate. The results indicate that the samples have great potential for application in
electronic devices.
|
|---|