| Summary: | Made available in DSpace on 2015-05-08T14:59:46Z (GMT). No. of bitstreams: 1
parte1.pdf: 1839351 bytes, checksum: 34e86046fc8cf8f52125675d2e7267f6 (MD5)
Previous issue date: 2009-03-03 === Coordenação de Aperfeiçoamento de Pessoal de Nível Superior === Melt spinnng processing is one of the most common processes to obtaining quasicrystaline structures. This is because of the fast cooling rate it imposes on the system, favoring such type of structure. This work deals with the production of quasycristaline phases (Al60Cu27,5Fe12,5 e Al57Cu27,5Fe12,5B3) via melt-spinning. The alloys were initially cast via induction melting under atmospheric air, with the designed chemical composition of the quasicrystals. Hence, the ribbons were produce by melt-spinning were characterized by means of x-ray diffraction and scanning electron microscopy. The results indicate that the icosahedral ψ - Al65Cu20Fe15 phase formed in both types of starting compositions. It seams that the boron contributes to stabilize the icosahedral phase. === O processo melt-spinning por imprimir altas taxas de resfriamento, é um dos principais meios para a obtenção de ligas com estrutura quasicristalinas, sendo o primeiro método utilizado para produzir materiais quasicristalinos. Neste trabalho utilizou-se este processo para a elaboração das ligas quasicristalinas Al(60-x)Cu25Fe15Bx, Al(60-x)Cu27,5Fe12,5Bx e Al(65-x)Cu20Fe15Bx (x=0 e x=3%at de boro). As ligas foram previamente fabricadas, por fusão, em atmosfera de argônio, em forno à indução, para em seguida serem submetidas ao processo melt-spinning , onde se obteve o material na forma de fita. As amostras foram caracterizadas por difração de raios-x e microscopia eletrônica de varredura. Os resultados indicaram a formação da fase icosaedral ψ - Al65Cu20Fe15 nas composições estudadas e uma provável contribuição do boro na produção dessa fase icosaedral
|
|---|