| Summary: | Made available in DSpace on 2015-05-08T15:00:01Z (GMT). No. of bitstreams: 1
arquivototal.pdf: 1709663 bytes, checksum: 35ce26ec1cf65f8e0507ea2d1c7adfd0 (MD5)
Previous issue date: 2009-10-13 === Coordenação de Aperfeiçoamento de Pessoal de Nível Superior === Cu-Al-Ni and Cu-Al-Be shape memory alloys were cast under ambient atmosphere, and characterized thought optical microscopy, X-ray diffraction, and differential scanning calorimetry. Superelasticity, and shape recovery were evaluated using mechanical tensile test. Thermomechanical properties of shape memory alloys used were obtained under different temperature range, in which was possible to conclude that Cu-Al-Ni alloy can be used as mechanical actuators for temperatures above 90ºC, as well as this alloy in particular should not be considered for application in temperatures below 30ºC. Differently of CuAlBe alloy that can be used in low temperatures, as well as in temperature superiors to 0ºC, as, for example, mechanical actuators. === Ligas Cu-Al-Ni e Cu-Al-Be forma elaboradas sob atmosfera ambiente e caracterizadas por microscopia, difração de R-X e Calorimetria Diferencial de varredura. Foram realizados nestas ligas ensaios de tração, recuperação de forma e superelasticidade. As propriedades termomecânicas destas ligas realizadas em diferentes temperaturas permitiu concluir que as ligas Cu-Al-Ni podem ser utilizadas como atuadores mecânicos para temperaturas acima de 90°C e que estas ligas não devem ser empregadas em temperaturas abaixo de 30°C. Podemos concluir também que as ligas Cu-Al-be podem ser utilizadas como atuadores mecânicos em temperaturas superiores a 0°C.
|
|---|