| Summary: | The dynamics of cross-linked polymers under stress, such as those thatmake up rubber, are still not well understood. A combination of coherent xrayhomodyne and heterodyne techniques is used in order to measure fluctuations of the system when stretched. The combination of both techniques allows for the measurement of flow patterns, as well as the random nature of the system. After data analysis, the results show that the measurements successfully captured this flow information. The flow velocity was discovered to have a time-dependent nature similar to that of the stress-strain curve. After the flow velocity was extracted, the random nature of the system was analysed. This random motion was discovered not to be dominated by conventional diffusion, but some slower random process. === La dynamique de polymères réticulés de stress, telles que celle qui compose le caoutchouc, n'est pas encore bien comprise. Une combinaison de techniques homodynes et hétérodynes de rayons x coherentes est utilisé pour mesurer les fluctuations du système, une fois étiré. La combinaison des deux techniques permet la mesure des régimes d'écoulement, ainsi que le caractère aléatoire du système. Après l'analyse des données, les résultats montrent que les mesures ont réussi à capturer cet information. La vitesse d'écoulement a été découverte de contenir une nature en fonction du temps semblable à celle de la courbe contrainte-déformation. Après la vitesse d'écoulement a été extraite, la nature aléatoire du système a été analysé. Cette motion a été découverte au hasard de ne pas être dominé par la diffusion classique, mais de certains processus aléatoires plus lents.
|
|---|