| Summary: | Thesis: Ph. D., Massachusetts Institute of Technology, Department of Electrical Engineering and Computer Science, 2018 === Cataloged from PDF version of thesis. === Includes bibliographical references (pages 152-163). === Photon upconversion is a process where two or more low-energy photons are converted into a single higher-energy photon. Upconversion that turns infrared photons into visible ones is particularly useful, having potential applications in photovoltaics, infrared sensing, and biological imaging. In this thesis, I present a solid-state thin-film device that converts infrared photons with wavelength up to 1.1 [mu]m into visible wavelengths around [lambda] = 610 nm. The device consists of a monolayer of lead sulfide colloidal nanocrystals (NCs) and a thin film of rubrene mixed with emissive DBP molecules. Upconversion is realized via triplet-triplet annihilation (TTA) in rubrene sensitized by the NCs. We demonstrate that compared to the previous all-molecular upconverting systems, the use of inorganic NCs helps extend the excitation wavelength into the infrared and offers simple wavelength tunability. === However, a monolayer of NCs has low infrared absorption, severely limiting the upconversion efficiency and necessitating a high excitation intensity. Here, by adding a silver back reflector with an optical spacer to the device structure, we achieve a five-fold increase in the NC absorption due to optical interference effects and an eleven-fold enhancement in the up-converted output. To extend the idea, we further introduce a distributed Bragg reflector at the front of the device. A resonant microcavity is formed with the NCs placed at the peak of a drastically enhanced optical field. The upconversion efficiency is improved by another order of magnitude, with threshold excitation intensity falling to 13 mW/cm² , which is below the available solar flux. At resonance, the device converts (0.06±0.01)% of incident photons at [lambda] = 980 nm into emitted higher-energy photons. In addition, we improve the upconversion efficiency by shortening the surface ligands on NCs. === With faster triplet transfer, the upconverting device attains higher intrinsic efficiency, converting (7±l)% of the absorbed photons at [lambda] = 808 nm into higher-energy emissive excitons in rubrene. This thesis demonstrates the feasibility of NC-sensitized infrared-to-visible upconversion in solid thin films under low excitation intensities comparable to the solar flux, and paves the way toward the practical utilization of TTA-based upconversion in photovoltaics, imaging, and sensing technologies. === by Mengfei Wu. === Ph. D. === Ph.D. Massachusetts Institute of Technology, Department of Electrical Engineering and Computer Science
|
|---|