Stress corrosion cracking and hydrogen embrittlement of thick section high strength low alloy steel
Thesis (Ocean E.)--Massachusetts Institute of Technology, Dept. of Ocean Engineering; and, (M.S.)--Massachusetts Institute of Technology, Dept. of Materials Science and Engineering, 1986. === 340909 === Bibliography: leaves 270-277. === An experimental study was conducted to evaluate the corrosion p...
Main Author: | Needham, William Donald |
---|---|
Other Authors: | Ronald G. Ballinger. |
Format: | Others |
Language: | English |
Published: |
Massachusetts Institute of Technology
2007
|
Subjects: | |
Online Access: | http://dspace.mit.edu/handle/1721.1/37166 http://hdl.handle.net/1721.1/37166 |
Similar Items
-
Stress corrosion cracking and hydrogen embrittlement of thick section high strength low alloy steel.
by: Needham, William Donald
Published: (2012) -
Corrosion fatigue crack growth and hydrogen embrittlement in high strength aluminium alloy 7150
by: Gingell, Andrew Donald Brian
Published: (1994) -
Crack formation, arrest and propagation in concrete slabs reinforced with closely spaced steel wires.
by: Crow, Hugh Enos
Published: (2010) -
Slow-strain-rate-hydrogen embrittlement and stress-corrosion cracking in ti-al binary alloys
by: Mauney, David Alexander
Published: (2006) -
Investigation of marine waterjet inlets during turning maneuvers
by: Duerr, Phillip S.
Published: (2016)