The effect of alloying elements on the ferritization treatment of ductile iron
碩士 === 國立中央大學 === 機械工程學系 === 85 === The effect of alloying elements on the ferrite fraction of ductile iron,after ferritizing treatment,had been fully investigated in this study.heat treatment conditions included austitization at 900 and 93...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
1997
|
Online Access: | http://ndltd.ncl.edu.tw/handle/42988929578778298044 |
id |
ndltd-TW-085NCU00489100 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-085NCU004891002015-10-13T17:59:41Z http://ndltd.ncl.edu.tw/handle/42988929578778298044 The effect of alloying elements on the ferritization treatment of ductile iron 合金元素對球墨鑄鐵肥粒鐵化熱處理之研究 Lee, Yih-Chyun 李逸群 碩士 國立中央大學 機械工程學系 85 The effect of alloying elements on the ferrite fraction of ductile iron,after ferritizing treatment,had been fully investigated in this study.heat treatment conditions included austitization at 900 and 930C for 1.5and 2 hours;ferritizing treatment at 700 and 730C for 1~3 hours. Experimental results showed that:(1).base ductile iron without addition of Cu or Ni developed a fully ferritematrix in a short ferritizing time but with a low hardness in the matrix.(2).Ductile iron added with 0.2% Cu showed a slightly longer ferritizing time to developed a giving fraction of ferrite comparing with base iron withoutaddition of Cu.(3).Ductile iron illustrated a fully ferrite matrix after ferritization treatment.The ferritizing time exceeding three hours was necessary,ifthe ductile iron added with 0.65% Cu or 0.5%-0.48%Ni.(4).According to the results of the regression analyses,nodule counts,alloyelements and carbon equivalent greatly affected the ferrite fraction inductile irons after ferritization treatment.The regression models were purposed to correlate the effect of alloyingelements,nodule counts and nodular diameter on the ferrite fraction developed for a giving ferritizing time. Teng-Shih Shih 施登士 1997 學位論文 ; thesis 200 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立中央大學 === 機械工程學系 === 85 === The effect of alloying elements on the ferrite fraction of
ductile iron,after ferritizing treatment,had been fully
investigated in this study.heat treatment conditions included
austitization at 900 and 930C for 1.5and 2 hours;ferritizing
treatment at 700 and 730C for 1~3 hours. Experimental results
showed that:(1).base ductile iron without addition of Cu or Ni
developed a fully ferritematrix in a short ferritizing time but
with a low hardness in the matrix.(2).Ductile iron added with
0.2% Cu showed a slightly longer ferritizing time to developed a
giving fraction of ferrite comparing with base iron
withoutaddition of Cu.(3).Ductile iron illustrated a fully
ferrite matrix after ferritization treatment.The ferritizing
time exceeding three hours was necessary,ifthe ductile iron
added with 0.65% Cu or 0.5%-0.48%Ni.(4).According to the results
of the regression analyses,nodule counts,alloyelements and
carbon equivalent greatly affected the ferrite fraction
inductile irons after ferritization treatment.The regression
models were purposed to correlate the effect of
alloyingelements,nodule counts and nodular diameter on the
ferrite fraction developed for a giving ferritizing time.
|
author2 |
Teng-Shih Shih |
author_facet |
Teng-Shih Shih Lee, Yih-Chyun 李逸群 |
author |
Lee, Yih-Chyun 李逸群 |
spellingShingle |
Lee, Yih-Chyun 李逸群 The effect of alloying elements on the ferritization treatment of ductile iron |
author_sort |
Lee, Yih-Chyun |
title |
The effect of alloying elements on the ferritization treatment of ductile iron |
title_short |
The effect of alloying elements on the ferritization treatment of ductile iron |
title_full |
The effect of alloying elements on the ferritization treatment of ductile iron |
title_fullStr |
The effect of alloying elements on the ferritization treatment of ductile iron |
title_full_unstemmed |
The effect of alloying elements on the ferritization treatment of ductile iron |
title_sort |
effect of alloying elements on the ferritization treatment of ductile iron |
publishDate |
1997 |
url |
http://ndltd.ncl.edu.tw/handle/42988929578778298044 |
work_keys_str_mv |
AT leeyihchyun theeffectofalloyingelementsontheferritizationtreatmentofductileiron AT lǐyìqún theeffectofalloyingelementsontheferritizationtreatmentofductileiron AT leeyihchyun héjīnyuánsùduìqiúmòzhùtiěféilìtiěhuàrèchùlǐzhīyánjiū AT lǐyìqún héjīnyuánsùduìqiúmòzhùtiěféilìtiěhuàrèchùlǐzhīyánjiū AT leeyihchyun effectofalloyingelementsontheferritizationtreatmentofductileiron AT lǐyìqún effectofalloyingelementsontheferritizationtreatmentofductileiron |
_version_ |
1718027595258265600 |