The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging
碩士 === 國立臺灣科技大學 === 營建工程技術學系 === 86 === This study discusses the fire resistance, mechanism of fire resist and durability of intumescent coating by small scale fire test, thermo-analysis, weatherometer test and salt spray test. From the results of tests, there are five conclusions that be made....
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
1998
|
Online Access: | http://ndltd.ncl.edu.tw/handle/43717852200912923435 |
id |
ndltd-TW-086NTUST512086 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-086NTUST5120862015-10-13T17:30:24Z http://ndltd.ncl.edu.tw/handle/43717852200912923435 The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging 膨脹型塗料之耐火性能研究─以耐火機理與老化前後之性能變化為對象 Wei Arthur 魏兆嶽 碩士 國立臺灣科技大學 營建工程技術學系 86 This study discusses the fire resistance, mechanism of fire resist and durability of intumescent coating by small scale fire test, thermo-analysis, weatherometer test and salt spray test. From the results of tests, there are five conclusions that be made. These include the following. 1.In the same section scale factor, it is positive relationship between fire resistance time and dry film thickness, but it isn''t linear dependence. 2.The cohesion and adhesion of intumesced coating are important factors of fire resistance. 3.According to the mechanism of fire resist, the typical curve of time and temperature during the fire test can be separated four different steps. It includes non-intumesced step, intumescing step, stable step and unstable step. 4.According to the result of weatherometer test, it should be satisfied when the intumescent coating is used in internal. 5.According to the result of salt spray test, the boundary of coating is a weak boundary of durability. Lin Ching-Yuan 林慶元 1998 學位論文 ; thesis 0 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立臺灣科技大學 === 營建工程技術學系 === 86 === This study discusses the fire resistance, mechanism of fire resist and durability of intumescent coating by small scale fire test, thermo-analysis, weatherometer test and salt spray test. From the results of tests, there are five conclusions that be made. These include the following. 1.In the same section scale factor, it is positive relationship between fire resistance time and dry film thickness, but it isn''t linear dependence. 2.The cohesion and adhesion of intumesced coating are important factors of fire resistance. 3.According to the mechanism of fire resist, the typical curve of time and temperature during the fire test can be separated four different steps. It includes non-intumesced step, intumescing step, stable step and unstable step. 4.According to the result of weatherometer test, it should be satisfied when the intumescent coating is used in internal. 5.According to the result of salt spray test, the boundary of coating is a weak boundary of durability.
|
author2 |
Lin Ching-Yuan |
author_facet |
Lin Ching-Yuan Wei Arthur 魏兆嶽 |
author |
Wei Arthur 魏兆嶽 |
spellingShingle |
Wei Arthur 魏兆嶽 The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging |
author_sort |
Wei Arthur |
title |
The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging |
title_short |
The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging |
title_full |
The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging |
title_fullStr |
The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging |
title_full_unstemmed |
The Fire Resistance of Intumescent Coating─The Mechanism of Fire Resist and the Influence of Accelerated Aging |
title_sort |
fire resistance of intumescent coating─the mechanism of fire resist and the influence of accelerated aging |
publishDate |
1998 |
url |
http://ndltd.ncl.edu.tw/handle/43717852200912923435 |
work_keys_str_mv |
AT weiarthur thefireresistanceofintumescentcoatingthemechanismoffireresistandtheinfluenceofacceleratedaging AT wèizhàoyuè thefireresistanceofintumescentcoatingthemechanismoffireresistandtheinfluenceofacceleratedaging AT weiarthur péngzhàngxíngtúliàozhīnàihuǒxìngnéngyánjiūyǐnàihuǒjīlǐyǔlǎohuàqiánhòuzhīxìngnéngbiànhuàwèiduìxiàng AT wèizhàoyuè péngzhàngxíngtúliàozhīnàihuǒxìngnéngyánjiūyǐnàihuǒjīlǐyǔlǎohuàqiánhòuzhīxìngnéngbiànhuàwèiduìxiàng AT weiarthur fireresistanceofintumescentcoatingthemechanismoffireresistandtheinfluenceofacceleratedaging AT wèizhàoyuè fireresistanceofintumescentcoatingthemechanismoffireresistandtheinfluenceofacceleratedaging |
_version_ |
1717780523272634368 |