Fatigue Behavior of Reactor Pressure Vessel Steels
博士 === 國立中央大學 === 機械工程研究所 === 91 === High-cycle, low-cycle fatigue tests and fatigue crack propagation measurements were conducted on SA533B1 steels, reactor pressure vessel (RPV) steels, with four levels of sulfur content (0.0062 wt%~ 0.035 wt%) at room temperature and 300 ℃. Efforts were made to s...